PVC Compound – Type PVC/ST2
Application standards: IEC 60227, TCVN 6610, IEC 60811.
| Properties | Test Method | Test Condition | Unit | Value |
| Mechanical and physical properties | ||||
| Without ageing | ||||
| Tensile Strength | IEC 60811-1-1 | – | Mpa | > 12,5 |
| Elongation | IEC 60811-1-1 | – | % | > 150 |
| After ageing | ||||
| Tesile strength Variation, maximum |
IEC 60811-1-2 | 800C, 168h | MPa % |
> 12,5 ± 25 |
| Elongation Variation, maximum |
IEC 60811-1-2 | 800C, 168h | % mg/cm2 |
> 150 ± 25 |
| Heat shock test | IEC 60811-3-1 | 1500C, 1h | – | no cracks |
PVC Compound – Type ST4
Application standards: IEC 60227, TCVN 6610, IEC 60811.
| Properties | Test Method | Test Condition | Unit | Value |
| Mechanical and physical properties | ||||
| Without ageing | ||||
| Tensile Strength | IEC 60811-1-1 | – | Mpa | > 12,5 |
| Elongation | IEC 60811-1-1 | – | % | > 150 |
| After ageing | ||||
| Tesile strength Variation, maximum |
IEC 60811-1-2 | 800C, 168h | MPa % |
> 12,5 ± 25 |
| Elongation Variation, maximum |
IEC 60811-1-2 | 800C, 168h | % mg/cm2 |
> 150 ± 25 |
| Heat shock test | IEC 60811-3-1 | 1500C, 1h | – | no cracks |
PVC Compound – Type ST5
Application standards: IEC 60227, TCVN 6610, IEC 60811.
| Properties | Test Method | Test Condition | Unit | Value |
| Mechanical and physical properties | ||||
| Without ageing | ||||
| Tensile Strength | IEC 60811-1-1 | – | Mpa | > 12,5 |
| Elongation | IEC 60811-1-1 | – | % | > 150 |
| After ageing | ||||
| Tesile strength Variation, maximum |
IEC 60811-1-2 | 800C, 168h | MPa % |
> 12,5 ± 25 |
| Elongation Variation, maximum |
IEC 60811-1-2 | 800C, 168h | % mg/cm2 |
> 150 ± 25 |
| Heat shock test | IEC 60811-3-1 | 1500C, 1h | – | no cracks |
PVC Compound – Type ST9
Application standards: IEC 60227, TCVN 6610, IEC 60811.
| Properties |
Test Method
|
Test Condition | Unit | Value |
| Mechanical and physical properties | ||||
| Without ageing | ||||
| Tensile Strength | IEC 60811-1-1 | – | Mpa | >10 |
| Elongation | IEC 60811-1-1 | – | % | > 150 |
| After ageing | ||||
| Tensile strength Variation, maximum |
IEC 60811-1-2 | 800C, 168h | MPa % |
>10 ± 20 |
| Elongation Variation, maximum |
IEC 60811-1-2 | 800C, 168h | % % |
> 150 ± 20 |
| Loss of mass | IEC 60811-1-2 | 800C, 168h | mg/cm2 | < 2 |
| After immersion in mineral oil | ||||
| Tensile strength, variation, maximium. | IEC 60811-3-2 | 900C,24h | % | ± 30 |
| Elongation, variation, maximium | IEC 60502-1 | |||
| 900C,24h | % | ± 30 | ||